| XR-5® 8130 Reinforced | Standard | Metric |
Base Fabric Type
ASTM D3776 | Polyester |
Base Fabric Weight (nominal)
ASTM D3776 | 6.5 oz/yd2 | 220 g/m2 |
Thickness
ASTM D751 | 30.0 mils min. | 0.76 mm min. |
Weight
ASTM D751 | 30.0 ± 2 oz/yd2 | 1017 ± 70 g/m2 |
Tear Strength
ASTM #D 1117, Trapezoid Tear | 35/35 lbf min. | 155/155 N min. |
Breaking Yield Strength
ASTM D751, Grab Tensile | 550/550 lbf min. | 2447/2447 N min. |
Low Temperature
ASTM D2136, 4 hr - 1/8" mandrel | Pass @ -30 º F | Pass @ -35 º C |
Dimensional Stability
ASTM D1204, 212º F - 1 hr | 1.5% max.
each direction |
Adhesion - Heat Sealed Seam
ASTM D751, Dielectric Weld | 35 lbf/2 in min. | 15 daN/5 cm min. |
Dead Load - Seam Shear Strength
ASTM D751
| 2 in seam, 4 hr, 1 in strip
210 lbf @ 70º F
105 lbf @ 160º F | 5 cm seam, 4 hr, 2.5 cm strip
934 N @ 21º C
467 N @ 70º C |
Bursting Strength
ASTM D751 Ball Tip | 650 lbf min.
800 lbf typical | 2892 N min.
3560 N typical |
Hydrostatic Resistance
ASTM D751, Method A | 800 psi min. | 5.51 MPa min. |
Blocking Resistance
ASTM D751 (180º F/82º C) | # 2 Rating max. |
Adhesion - Ply
ASTM D413 | 15 lbf/in min.
or Film Tearing Bond | 13 daN/5 cm min.
or Film Tearing Bond |
Bonded Seam Strength
ASTM D751 as modified by NSF 54
| 550 lbf min. | 2447 N min. |
Abrasion Resistance
ASTM D3389 (H-18 Wheel, 1000 g load) | 2000 cycles (min.) before fabric exposure
50 mg/100 cycles max weight loss |
Weathering Resistance
ASTM G23 (Carbon-Arc) | 8,000 hrs (min.) - No appreciable changes
or stiffening or cracking of coating |
Water Absorption
ASTM D471, Section 12, 7 days | 0.025 kg/m2 max. @ 70º F/21º C
0.14 kg/m2 max. @ 212º F/100º C |
Wicking
Shelter-Rite® Procedure | 1/8 in max. | 0.3 cm max. |
Puncture Resistance
ASTM D4833 | 250 lbf min. | 1112 N min. |
Coefficient of Thermal Expansion/Contraction
ASTM D696 | 8 x 10-6 in/in/ºF max. | 1.4 x 10-5 cm/cm/ºC max. |